|Place of Origin:||Hunan, China (Mainland)|
|Model Number:||YU09 Tungsten Carbide Hardfacing Electrodes|
|Minimum Order Quantity:||Negotiation|
|Packaging Details:||Boxes Inside and Cartons Outside|
|Delivery Time:||20~30 Days after Your Order Confirmed|
|Payment Terms:||L/C, T/T|
|Supply Ability:||20000 Kilograms per month|
|Product Name:||Tungsten Carbide Hardfacing Electrodes||Material:||100% Virgin Tungsten Carbide|
|Application:||Low Carbon Steel Structure||Density:||14.36-14.50 G/cm³|
|Hardness HV3:||≥1950||Grain Size Of WC:||0.2-0.4 Um|
tungsten carbide brazing rod,
alloy welding rods
Nickel Tungsten Carbide Hardfacing Electrodes / Tungsten Carbide Welding Rods
Tungsten Carbide Hardfacing Electrodes advantage
High hardness, high melting point, high wear resistance and high heat resistance.
Tungsten Carbide Hardfacing Electrodes Application :
Tungsten Carbide Hardfacing Electrodes is suitable for welding of low carbon steel structure, especially for the welding of thin plate steel with short discontinuous weld and requirement of smooth welding pass.
Tungsten Carbide Hardfacing Electrodes Grade
|Grade||Chemical composition||Physical data||Structure|
of WC (um)
Q1: Are you a factory or a trading company?
A: We are a factory. We have been focusing on Tungsten Carbide for over 20 years.
Q2:What is your principle for the samples?
A: We offer free samples if you are willing to pay the freight.
Q3:What is your delivery time?
A: Generally it is 5 to 7 days if your required goods are in stock, otherwise it takes 20 to 30 days when there is no stock.
Q4:Do you have any test reports or certificates?
A: Yes, we can offer certificate of ISO9000:2008, we also report our test results for your reference.
Q5: Do you provide after-sale service?
A: Yes. So if you find any problem after using our cutting tools, please do not hesitate to tell us, we’ll help you to solve it as soon as possible. Your any feedback to products is our way to improvement
Packaging & Delivery:
Plastic Boxes Inside and Cartons Outside
Contact Person: Mr. Zhou